| Hardness: | 60-65HRC | Breakage Rate: | ≤1% |
|---|---|---|---|
| Impact Value: | ≥12J/cm² | Drop Times: | ≥12000 |
| Diameter: | 2inch 3inch | Micro Structure: | M+C |
| High Light: | 2 Inch Ball Mill Grinding Media,3 Inch Ball Mill Grinding Media,60HRC Forged Steel Balls |
||
COMPANY ENVIOMENT
PRODUCTS INTRODUCTION
| Series/Element | C(%) | Si(%) | Mn(%) | Cr(%) | Cu(%) | Mo(%) | P(%) | S(%) |
| 45# | 0.42-0.85 | 0.17-0.37 | 0.50-0.80 | 0-0.25 | 0-0.25 | 0-0.30 | 0-0.035 | 0-0.035 |
| 40Mn | 0.37-0.44 | 0.17-0.37 | 0.70-1.0 | 0-0.25 | 0-0.25 | 0-0.30 | 0-0.035 | 0-0.035 |
| 40Mn2 | 0.37-0.44 | 0.17-0.37 | 1.40-1.80 | 0-0.25 | 0-0.25 | 0-0.30 | 0-0.035 | 0-0.035 |
| 70Mn | 0.65-0.75 | 0.17-0.37 | 0.90-1.20 | 0-0.25 | 0-0.25 | 0-0.30 | 0-0.035 | 0-0.035 |
| 70Mn2 | 0.65-0.75 | 0.20-0.45 | 1.4-1.8 | 0-0.25 | 0-0.25 | 0-0.30 | 0-0.035 | 0-0.035 |
| 40Cr | 0.37-0.45 | 0.17-0.37 | 0.50-0.8 | 0.80-1.1 | 0-0.25 | 0-0.30 | 0-0.035 | 0-0.035 |
| 70Cr2 | 0.65-0.75 | 0.20-0.30 | 0.75-0.90 | 0.55-0.70 | 0-0.25 | 0-0.30 | 0-0.030 | 0-0.030 |
| B1 | 0.52-0.65 | 0.17-0.37 | 0.60-1.2 | 0-0.25 | 0-0.25 | 0-0.30 | 0-0.035 | 0-0.035 |
| B2 | 0.70-0.80 | 0.17-0.37 | 0.70-0.8 | 0.50-0.60 | 0-0.25 | 0-0.30 | 0-0.035 | 0-0.035 |
| B3 | 0.58-0.66 | 1.20-1.60 | 0.65-0.80 | 0.70-0.90 | 0-0.25 | 0-0.30 | 0-0.035 | 0-0.035 |
| B-6 | 0.75-0.85 | 0.2-0.40 | 0.90-1.0 | 0.85-0.95 | 0-0.25 | 0.06-0.13 | 0-0.035 | 02-0.035 |
| B-6A | 0.82-0.95 | 0.20-0.40 | 0.92-1.02 | 0.80-0.95 | 0-0.25 | 0.06-0.10 | 0-0.035 | 0-0.035 |
| B-7 | 0.35-0.40 | 0.17-0.37 | 0.70-0.80 | 0.90-1.0 | 0-0.25 | 0-0.30 | 0-0.035 | 0-0.035 |
| BV | 1-1.06 | 0.17-0.37 | 0.9-1.0 | 0.55-0.65 | 0-0.25 | 0-0.30 | 0-0.035 | 0-0.035 |
| GCr15 | 0.95-1.05 | 0.15-0.35 | 0.20-0.40 | 1.30-1.65 | 0-0.25 | 0-0.10 | 0-0.027 | 0-0.20 |
| 16Mn | 0.13-0.19 | 0.2-0.6 | 1.2-1.6 | 0-0.30 | 0-0.25 | --- | 0-0.03 | 0-0.03 |
| Diameter Tolerance(mm) | 20-25mm | 30-60mm | 70-90mm | 100-140mm | 150mm | ||
| ±1 | ±1.5 | +2,-2 | +2.5,-2 | +3,-2 | |||
| Roundness tolerance(%) | ≤1% | ≤1% | ≤1.5% | ≤2% | ≤2% | ||
|
|
|||||||
|
Forged Steel Ball Production Process |
1)Fully automatic production line of hot rolling steel ball Raw material testing→Material on storage rack→automatic continued feeding device→furnace heating→enter into rolling ball machine→automatic isothermal transfer→quenching system→steel ball heating preservation device→finished steel ball testing→package→transport to warehouse
2)Automatic production line of hot forging steel ball Raw material testing→Material on storage rack→furnace heating→hot cutting→preforging→enter into rolling ball machine →automatic isothermal system transport→quenching system→steel ball heating preservation device→finished steel ball testing→package→transport towarehouse
3)Traditional production line of forged steel ball Raw material testing→Cutting raw material→furnace heating→forging→automatic isothermal system→quenching system→steel ball heating preservation device→finished steel ball testing→package→transport to warehouse
|
||||||